Table 2.
| Alloy |
gammma-prime
atomic
fraction |
Lattice
misfit
(%) |
Density
(g/cm3) |
Creep
rup.life(h) |
***Hot
corrosion
rate |
| *CC |
**SC |
| CC alloys |
| Incone1713C |
0.55 |
-0.21 |
7.96 |
51 |
- |
8.3 |
| IN 738LC |
0.41 |
0.23 |
8.21 |
24 |
- |
1 |
| B1900Hf |
0.54 |
-0.07 |
8.21 |
189 |
- |
2.4 |
| MarM200 |
0.61 |
0.08 |
8.50 |
298 |
- |
2.3 |
| TM-321 |
0.61 |
0.21 |
8.82 |
767 |
- |
1.5 |
| DS alloys |
| MarM247DS |
0.64 |
0.17 |
8.57 |
(688) |
- |
0.7 |
| Rene 125 |
0.63 |
0.14 |
8.51 |
(533) |
- |
0.4 |
| TMD-5 |
0.59 |
0.19 |
8.96 |
(1094) |
- |
1.4 |
| SC alloys |
| Alloy 454 |
0.64 |
0.58 |
8.68 |
(591) |
209 |
(3.6) |
| NASAIR100 |
0.72 |
-0.13 |
8.59 |
(551) |
420 |
(4.1) |
| SRR 99 |
0.67 |
0.12 |
8.50 |
(505) |
367 |
(1.9) |
| RR2000 |
0.57 |
-0.02 |
7.90 |
(99) |
181 |
(0.8) |
| Rene N4 |
0.56 |
0.39 |
8.51 |
(249) |
52 |
(1.2) |
| CMSX-2 |
0.61 |
0.29 |
8.61 |
(496) |
763 |
(4.6) |
| MXON |
0.69 |
0.01 |
8.62 |
(626) |
728 |
(9.1) |
| MMT143 |
0.60 |
-0.38 |
8.61 |
(930) |
>10000 |
(188.5) |
| TMS-1 |
0.64 |
0.16 |
9.16 |
(1492) |
1747 |
(8.9) |
| TMS-12 |
0.60 |
0.33 |
9.06 |
(894) |
3486 |
(10.5) |
| SC 83 |
0.55 |
0.18 |
8.84 |
(498) |
2168 |
(21.2) |
| PM alloys |
| MERL 76 |
0.49 |
0.20 |
8.05 |
(50) |
- |
0.6 |
| Rene 95 |
0.48 |
0.04 |
8.26 |
(31) |
- |
5.3 |
| AF 115 |
0.60 |
0.01 |
8.34 |
(158) |
- |
0.8 |
| TMP-3 |
0.57 |
0.16 |
8.26 |
(75) |
- |
6.3 |
| ODS alloys(Base metal) |
| MA 6000 |
0.49 |
-0.03 |
8.21 |
(63) |
- |
1.6 |
| TMO-2 |
0.47 |
0.30 |
8.98 |
(281) |
- |
8.3 |
* at 1000 deg.C-118MPa, assuming CC structure, grain size about 3 mm.
** at 1040 deg.C-137MPa, assuming solutioned and aged SC structure, tensile axis within 10 deg.C of <100>.
*** Penetraeion depth in burner rig test at 850 deg.C, normalized by IN738LC(=1).