Table 2.
ALLOY PWA1480 PHASE(AT 900 deg.C) & PROPERTY CALCULATION
| | Ni | Co | Cr | Mo | W | Al | Ti | Nb | Ta | Hf | Re |
|---|
| GP | 68.73 | 3.05 | 3.19 | .00 | 0.86 | 15.83 | 2.72 | .00 | 5.62 | .00 | .00 |
|---|
| G | 57.59 | 8.81 | 26.45 | .00 | 2.13 | 3.30 | 0.48 | .00 | 1.25 | .00 | .00 |
|---|
| ATPCT | 64.66 | 5.15 | 11.68 | .00 | 1.32 | 11.25 | 1.90 | .00 | 4.03 | .00 | .00 |
|---|
| WTPCT | 62.50 | 5.00 | 10.00 | .00 | 4.00 | 5.00 | 1.50 | .00 | 12.00 | .00 | .00 |
|---|
| F.GP | LAT.GP(A) | NV.GP | LIQ(C) | SOL2(C) | H.COR.C | YS(MPA) | LIFE.CC(H) |
|---|
| 0.635 | 3.603 | 2.406 | 1377.7 | 1288.9 | 1476.17 | 572.7 | 591.3 |
| DENSITY | LAT.G(A) | NV.G | SOL1(C) | SOLV(C) | H.COR.B | UTS(MPA) | LIFE.SC(H) |
|---|
| 8.680 | 3.582 | 2.217 | 1336.2 | 1325.9 | 3.64 | 693.1 | 370.1 |
| SI | LM(%) | NV.G-NVC | RANGE(C) | WDW(C) | EL(%) | SPC.STRGTH |
|---|
| 1.263 | 0.583 | 0.059 | 41.5 | -37.0 | 7.2 | 11.67 |
ALLOY PWA1484 PHASE(AT 900 deg.C) & PROPERTY CALCULATION
| | Ni | Co | Cr | Mo | W | Al | Ti | Nb | Ta | Hf | Re |
|---|
| GP | 66.63 | 6.49 | 1.80 | 0.60 | 1.69 | 18.22 | .00 | .00 | 4.30 | 0.05 | 0.21 |
|---|
| G | 57.81 | 16.89 | 12.50 | 2.38 | 2.57 | 4.65 | .00 | .00 | .95 | 0.01 | 2.24 |
|---|
| ATPCT | 63.18 | 10.56 | 5.98 | 1.30 | 2.03 | 12.92 | .00 | .00 | 2.99 | 0.03 | 1.00 |
|---|
| WTPCT | 59.60 | 10.00 | 5.00 | 2.00 | 6.00 | 5.60 | .00 | .00 | 8.70 | 0.10 | 3.00 |
|---|
| F.GP | LAT.GP(A) | NV.GP | LIQ(C) | SOL2(C) | H.COR.C | YS(MPA) | LIFE.CC(H) |
|---|
| 0.609 | 3.596 | 2.384 | 1411.4 | 1337.0 | 19293.62 | 557.0 | 843.8 |
| DENSITY | LAT.G(A) | NV.G | SOL1(C) | SOLV(C) | H.COR.B | UTS(MPA) | LIFE.SC(H) |
|---|
| 8.914 | 3.587 | 1.894 | 1384.5 | 1297.8 | 10.80 | 643.8 | 1284.6 |
| SI | LM(%) | NV.G-NVC | RANGE(C) | WDW(C) | EL(%) | SPC.STRGTH |
|---|
| 1.209 | 0.243 | 0.293 | 27.0 | 39.2 | 8.4 | 14.56 |
ALLOY TMS-63 PHASE(AT 900 deg.C) & PROPERTY CALCULATION
| | Ni | Co | Cr | Mo | W | Al | Ti | Nb | Ta | Hf | Re |
|---|
| GP | 72.69 | .00 | 2.80 | 2.12 | .00 | 18.39 | .00 | .00 | 4.00 | .00 | .00 |
|---|
| G | 71.05 | .00 | 15.33 | 8.33 | .00 | 4.34 | .00 | .00 | 0.89 | .00 | .00 |
|---|
| ATPCT | 72.04 | .00 | 7.83 | 4.60 | .00 | 12.77 | .00 | .00 | 2.76 | .00 | .00 |
|---|
| WTPCT | 71.42 | .00 | 6.88 | 7.46 | .00 | 5.82 | .00 | .00 | 8.42 | .00 | .00 |
|---|
| F.GP | LAT.GP(A) | NV.GP | LIQ(C) | SOL2(C) | H.COR.C | YS(MPA) | LIFE.CC(H) |
|---|
| 0.600 | 3.593 | 2.344 | 1376.4 | 1330.5 | 27396.36 | 504.1 | 388.0 |
| DENSITY | LAT.G(A) | NV.G | SOL1(C) | SOLV(C) | H.COR.B | UTS(MPA) | LIFE.SC(H) |
|---|
| 8.481 | 3.592 | 1.957 | 1336.6 | 1288.8 | 31.24 | 573.7 | 3591.4 |
| SI | LM(%) | NV.G-NVC | RANGE(C) | WDW(C) | EL(%) | SPC.STRGTH |
|---|
| 1.100 | 0.008 | 0.122 | 39.7 | 41.7 | 4.7 | 15.30 |