Table 1

Table 1.

log( $τ$ )=3.00	-0.059X_Co^'	-0.161X_Cr^'	+0.027X_Mo^'	+0.254X_W^'
	+0.087X_Ti^'	+0.298X_Nb^'	0.420X_Ta^'	-0.012F	-3.098 $δ$
t-test^*	0.1	-	-	10
t-test^*	-	10	0.1	-	1
F-test^*			0.5
MCC			0.92
gamma-prime composition X_i^'(at%),gamma-prime fraction F (at%), and gamma/gamma-prime lattice misfit delta(%) ^* Probabilities(%) of error are smaller than the shown values.